Mechanical Degradation of Different Classes of Composite Resins Aged in Water, Air, and Oil.

A significant deterioration of the properties can drastically compromise the survival rate of restorative materials. The aim of this study was to assess flexural strength and hardness of three composite classes: hybrid composite resin (HCR), nanoparticulate composite resin (NCR), and silorane-based composite resin (SBCR). One hundred specimens were prepared for hardness testing by using a split metallic mold measuring 10 mm in diameter and 2 mm deep. Twenty specimens were prepared for each restorative material, randomly assigned for storage in air, distilled water, or mineral oil. After intervals of 24 hours, 30, 60, 90, and 120 days, hardness and flexural strength tests were initially compared in two levels: "storage medium" and "time" within each material group. A two-way analysis of variance was performed (p<0.05) on the variables "material" and "storage time" (p<0.05). The HCR showed to be stable with regard to the evaluation of flexural strength and hardness (p<0.05). A significant reduction occurs for the NCR in comparison to the other groups (p<0.05). The NCR presented the lowest values of hardness and flexural strength kept on water over time. The characteristics of material showed a strong influence on the decrease of the mechanical properties analyzed.

Pre-heating mitigates composite degradation

ABSTRACT Dental composites cured at high temperatures show improved properties and higher degrees of conversion; however, there is no information available about the effect of pre-heating on material degradation. Objectives This study evaluated the effect of pre-heating on the degradation of composites, based on the analysis of radiopacity and silver penetration using scanning electron microscopy/energy-dispersive X-ray spectroscopy (SEM/EDS). Material and Methods Thirty specimens were fabricated using a metallic matrix (2x8 mm) and the composites Durafill VS (Heraeus Kulzer), Z-250 (3M/ESPE), and Z-350 (3M/ESPE), cured at 25°C (no pre-heating) or 60°C (pre-heating). Specimens were stored sequentially in the following solutions: 1) water for 7 days (60°C), plus 0.1 N sodium hydroxide (NaOH) for 14 days (60°C); 2) 50% silver nitrate (AgNO3) for 10 days (60°C). Specimens were radiographed at baseline and after each storage time, and the images were evaluated in gray scale. After the storage protocol, samples were analyzed using SEM/EDS to check the depth of silver penetration. Radiopacity and silver penetration data were analyzed using ANOVA and Tukey’s tests (α=5%). Results Radiopacity levels were as follows: Durafill VS<Z-350<Z-250 (p<0.05). The depth of silver penetration into the composites ranked as follows: Durafill VS>Z-350>Z-250 (p<0.05). After storage in water/NaOH, pre-heated specimens presented higher radiopacity values than non-pre-heated specimens (p<0.05). There was a lower penetration of silver in pre-heated specimens (p<0.05). Conclusions Pre-heating at 60°C mitigated the degradation of composites based on analysis of radiopacity and silver penetration depth.

Pre-heating mitigates composite degradation.

Dental composites cured at high temperatures show improved properties and higher degrees of conversion; however, there is no information available about the effect of pre-heating on material degradation. Objectives This study evaluated the effect of pre-heating on the degradation of composites, based on the analysis of radiopacity and silver penetration using scanning electron microscopy/energy-dispersive X-ray spectroscopy (SEM/EDS). Material and Methods Thirty specimens were fabricated using a metallic matrix (2x8 mm) and the composites Durafill VS (Heraeus Kulzer), Z-250 (3M/ESPE), and Z-350 (3M/ESPE), cured at 25°C (no pre-heating) or 60°C (pre-heating). Specimens were stored sequentially in the following solutions: 1) water for 7 days (60°C), plus 0.1 N sodium hydroxide (NaOH) for 14 days (60°C); 2) 50% silver nitrate (AgNO3) for 10 days (60°C). Specimens were radiographed at baseline and after each storage time, and the images were evaluated in gray scale. After the storage protocol, samples were analyzed using SEM/EDS to check the depth of silver penetration. Radiopacity and silver penetration data were analyzed using ANOVA and Tukey's tests (α=5%). Results Radiopacity levels were as follows: Durafill VSZ-350>Z-250 (p<0.05). After storage in water/NaOH, pre-heated specimens presented higher radiopacity values than non-pre-heated specimens (p<0.05). There was a lower penetration of silver in pre-heated specimens (p<0.05). Conclusions Pre-heating at 60°C mitigated the degradation of composites based on analysis of radiopacity and silver penetration depth.

Effect of carbamide peroxide bleaching gel on composite resin flexural strength and microhardness.

This study investigated the effect of 16% carbamide peroxide (Whiteness Perfect/FGM) on the Vickers microhardness and flexural strength of the restorative composites Filtek Z100 (hybrid), Filtek Z350 (nanofill), Brilliant (micro-hybrid) and Opallis (micro-hybrid). Disc-shaped (4x2 mm; n=5) and bar-shaped (12x2x1 mm; n=10) specimens of each restorative material were randomly divided into 2 groups: (G1) 16 weeks stored in distilled water; (G2) 16 weeks stored in distilled water, with 16% carbamide peroxide application during 6 h per day for the last 4 weeks. The mechanical properties were evaluated using a Vickers microhardness tester and a mechanical testing machine. Data were analyzed by two-way ANOVA and Tukey's (HSD) post-hoc test (α=0.05). Filtek Z100 presented the highest microhardness value, followed by Filtek Z350 and finally by Brilliant and Opallis (p=0.00). Filtek Z100 and Brilliant exhibited the highest flexural strength value, followed by Filtek Z350 and Opallis (p=0.00). Bleaching treatment decreased significantly microhardness of Brilliant and Opallis (p=0.00). The flexural strength of all studied materials was not affected by the home bleaching (p=0.28).

Resistência à flexão em porcelana feldspática: efeito da ciclagem mecânica e limite de fadiga pelo método escada / Flexural strength of feldspathic porcelain: effect of mechanical cycling and fatigue limit by the staircase method

Este estudo avaliou o limite de fadiga (LF), determinado pelo método escada, e o efeito da ciclagem mecânica sobre a resistência à flexão (RF) da porcelana feldspática Duceragold. Corpos de prova (25 x 5 x 2 mm) foram confeccionados de acordo com as instruções do fabricante e submetidos ao ensaio de RF (n = 10), em três pontos. Para determinação do LF (n = 30), foram utilizados carregamento inicial de 60% da RF, tensão incremental de 3% da RF, 10.000 ciclos e 2 Hz. Os dados foram submetidos à Anova e teste de Tukey (p < 0,05). Embora os ciclos propostos não tenham reduzido estatisticamente a RF, análises fractográficas evidenciaram estrias, sinais característicos de fadiga mecânica.

This study evaluated the fatigue limit (FL) by the staircase method and the effect of mechanical cycling on the flexural strength (FS) of Duceragold feldspathic porcelain. Specimens (25 x 5 x 2 mm) were made according to manufacturer’s directions and submitted to t hree-point fl exural s trength t est (n = 10). To d etermine FL (n = 30; 10,000 cycles; 2 Hz), an initial loading of 60% of the FS and an incremental loading (step) of 3% of the FS were used. Data were analyzed by Anova and Tukey´s test (p < 0.05). Although the proposed cycles have not reduced FS significantly, fractography analysis showed striation, characteristic signs of mechanical fatigue.

Effect of Carbamide Peroxide Bleaching Gel on Composite Resin Flexural Strength and Microhardness

This study investigated the effect of 16% carbamide peroxide (Whiteness Perfect/FGM) on the Vickers microhardness and flexural strength of the restorative composites Filtek Z100 (hybrid), Filtek Z350 (nanofill), Brilliant (micro-hybrid) and Opallis (micro-hybrid). Disc-shaped (4x2 mm; n=5) and bar-shaped (12x2x1 mm; n=10) specimens of each restorative material were randomly divided into 2 groups: (G1) 16 weeks stored in distilled water; (G2) 16 weeks stored in distilled water, with 16% carbamide peroxide application during 6 h per day for the last 4 weeks. The mechanical properties were evaluated using a Vickers microhardness tester and a mechanical testing machine. Data were analyzed by two-way ANOVA and Tukey's (HSD) post-hoc test (α=0.05). Filtek Z100 presented the highest microhardness value, followed by Filtek Z350 and finally by Brilliant and Opallis (p=0.00). Filtek Z100 and Brilliant exhibited the highest flexural strength value, followed by Filtek Z350 and Opallis (p=0.00). Bleaching treatment decreased significantly microhardness of Brilliant and Opallis (p=0.00). The flexural strength of all studied materials was not affected by the home bleaching (p=0.28).

Este estudo investigou o efeito do peróxido de carbamida a 16% (Whiteness Perfect/FGM) na dureza Vickers e resistência à flexão dos compósitos restauradores Filtek Z100 (híbrida), Filtek Z350 (nanoparticulada), Brilliant (micro-híbrida) e Opallis (micro-híbrida). Espécimes em forma de disco (4x2 mm; n=5) e de barra (12x2x1 mm; n=10) de cada material restaurador foram distribuídos aleatoriamente em 2 grupos: (G1) 16 semanas em água destilada; (G2) armazenamento em água destilada durante 16 semanas, com aplicação do peróxido de carbamida a 16% por 6 h diárias nas últimas 4 semanas. As propriedades mecânicas foram avaliadas em microdurômetro Vickers e máquina de ensaios mecânicos. Os dados foram analisados por ANOVA a 2 critérios e teste de Tukey (α=0,05). Filtek Z100 apresentou o maior valor de dureza, seguido por Filtek Z350 e, finalmente, por Brilliant e Opallis (p=0,00). Filtek Z100 e Brilliant mostraram o maior valor de resistência à flexão, seguido por Filtek Z350 e Opallis (p=0,00). O clareamento diminuiu significantemente a dureza das resinas Brilliant e Opallis (p=0,00). A resistência à flexão dos materiais estudados não foi afetada pelo clareamento caseiro (p=0,28).

Shear bond strength of different repair systems to titanium after water aging.

This study evaluated the shear bond strength (SBS) and stability of commercially pure titanium (CP Ti)/repair material interfaces promoted by different repair systems. One hundred CP Ti cast discs were divided into five repair system groups: 1) Epricord (EP); 2) Bistite II DC (BT); 3) Cojet (CJ); 4) Scotchbond Multi-Purpose Plus (SB) (control group); and 5) Cojet Sand plus Scotchbond Multi-Purpose Plus (CJSB). The specimens were stored in distilled water for 24 hours at 37°C, thermal cycled (5000 cycles, 5°-55°C) and stored under the same conditions for either 24 hours or six months (n=10). SBS was tested and the data were analyzed by two-way analysis of variance (ANOVA) and Tukey test (α=.05). Failure mode was determined with a stereomicroscope (20×). The repair system, storage time, and their interaction significantly affected the SBS (p<0.001). At 24 hours, CJSB exhibited the highest SBS value, followed by CJ. At six months, these two groups had similar mean SBS (p>0.05) and higher means in comparison to the other groups. For both storage times, BT presented the lowest SBS, while the EP and SB groups did not differ significantly from one another (p>0.05). There were no significant differences in SBS between the storage times for the groups EP and CJ (p>0.05). The groups BT, SB, and CJSB showed 100% adhesive failure, irrespective of storage time. The CJSB group showed the highest SBS at both storage times. At six months, the CJ group exhibited a similar SBS mean value when compared to the CJSB group. Water storage adversely affected the groups BT, SB (control group), and CJSB. Considering SBS values, stability, and the failure mode simultaneously, the CJ group showed the best CP Ti repair performance.

Efeito de diferentes métodos dedesinfecção sobre a dureza Vickers de porcelana feldspática / Effect af different disinfectian methads an Vickers hardness af feldspathic porcelain

O trânsito de peças protéticas entre laboratórios de prótese e consultórios odontológicos pode constituir-se em importante fonte de contaminação cruzada. Foi objetivo deste estudo, avaliar o efeito de diferentes métodos de desinfecção sobre a dureza Vickers da porcelana felds¬pática Duceragold (DeguDent), material largamente empregado em trabalhos protéticos. Corpos de prova em forma de disco (5,Ox2,5mm; n=5) foram confeccionados segundo instruções do fabricante, incluídos em RAAQ, polidos e submetidos a dois ciclos dos seguintes tratamentos: 1) 30 minutos, em solução de hipoclorito de sódio a 1%; 2) 30 minutos, em álcool etílico a 70%; 3) 5 minutos, em solução de digluconato de clorexidina a 2%; 4) 60 minutos, em estufa a 170°(; 5) 20 minutos, em autoclave a 120°C; e 6) 5 minutos, em micro-ondas a 650 W de potência. Os resultados, submetidos à análise de variância (p<0,05), mostraram redução significativa de dureza (p=O,015J, para os grupos álcool etílico, clorexidína e estufa, já no primeiro ciclo de desinfecção. Considerando-se a resistência mecânica superficial, peças protéticas confeccionadas em porcelana feldspática poderão ser submetidas à desinfecção por meio de hipoclorito de t sódio a 1%, por 30 minutos; autoelave a 120°C, por 20 minutos; ou forno de micro-ondas a 650W, por 5 minutos.

Due to the possibility of cross-contamination through the dental laboratory and dentaloffice, it was appropriate to evaluate the effect of different disinfection methods on the Vickers hardness of Duceragold feldspathic porcelain (DeguDent). Discs (5mm dia meter x 2.5 thick; n=5)) were made according the manufacturer's instructions, embedded, polished and submit¬ted to 2 cyeles of one of the following treatments: 1) 1% sodium hypochlorite solution for 30 min; 2) 70% ethyl alcohol for 30 min; 3) 2% clorhexidine solution for 5 min; 4) oven at 170°C for 60 min;:J)~utoclave at 120°C for 20 min; 6) 650W microwave irradiation for 5 mino The results, submitted to two-way ANOVA (p<0.05J, showed reduction of hardness (p=0015) only for groups 2, 3 and 4. From a mechanical view, feldspathic porcelain indirect restorations may be disinfected by immersion in 1% sodium hypochlorite for 30 minutes, autoclave at 120°C for 20 minutes or 650W microwave irradiation for 5 minutes.

Efeito das dimensões dos corpos de prova na resistência à flexão de compósitos restauradores / Effect of specimen size on flexural strength of restorative composites

O objetivo deste estudo foi avaliar, em relação à norma ISO, o efeito da redução das dimensões dos corpos de prova na resistência à flexão, em três pontos, dos compósitos restauradores de nanopartículas (Filtek Supreme - 3M ESPE) e micro-híbrido (Filtek Z-250 - 3M ESPE). Foram confeccionados 40 corpos de prova para cada material com asseguintes dimensões de comprimento, largura e espessura (n = 10): 1) 20 × 2 × 2 mm (ISO 4049); 2) 10 × 2 × 1 mm; 3) 10 × 1 × 1 mm; 4) 8 × 0,8 × 0,8 mm. Os compósitos foram inseridos em único incremento em matrizes metálicas bipartidas, correspondentes a cada dimensão avaliada, e fotoativados. Os corpos de prova foram armazenados a 37 ± 1 °C, em ambiente seco e protegido de luz, durante 7 dias. Posteriormente, foi realizado o ensaio de resistência à flexão, em três pontos, usando o equipamento MTS 810, com célula de carga de 10 kN e velocidade de 0,5 mm/min. Os resultados mostraram variabilidade significativa para as dimensões avaliadas (p = 0,00), com valores, em relação à norma ISO (116,700 MPa), estatisticamente superiores para os corpos de prova de 10 × 1 × 1 mm (142,530 MPa), semelhantes para os de 10 × 2 × 1 mm (115,815 MPa) e inferiores para os de 8 × 0,8 × 0,8 mm (86,650 MPa).Houve igualdade estatística (p = 0,08) para os compósitos estudados (Filtek Supreme, 125,270 MPa; Filtek Z-250, 108,130 MPa). Corpos de prova de 10 × 2 × 1 mm proporcionaram, com menor consumo de material, energia e tempo, valores de resistência à flexão equivalentes àqueles obtidos nas dimensões preconizadas pela norma ISO 4049.

The aim of this study was to evaluate the influence of specimen size, in comparison with the ISO Standard, on the three point flexural strength of resin composite restorative materials Filtek Supreme and Filtek Z-250. Fortyspecimens were fabricated for each material with the following length, width and thickness measurements (n = 10): 1) 20 × 2 × 2 mm (ISO 4049); 2) 10 × 2 × 1 mm; 3) 10 × 1 × 1 mm; 4) 8 × 0.8 × 0.8 mm. The composites were inserted in a single increment into two-piece metal device and light-polymerized. The specimens were dry stored at 37 ± 1 °C and protected from light for 7 days. After this period, flexural strength was measured by three-point flexure test using MTS 810 equipment, with a load cell of 10 kN at a speed of 0.5 mm/min. For the evaluated sizes, the results showed significant variability (p = 0.00) with values when compared with the ISO Standard (116.700 MPa), being statistically higher for the test specimens measuring 10 × 1 × 1 mm (142.530 MPa), similar for those of 10 × 2 × 1 mm (115.815 MPa) and lower for those of 8 × 0.8 × 0.8 mm (86.650 MPa). There was statistical equality (p = 0.08) for the studied composites (Filtek Supreme, 125.270 MPa; Filtek Z-250, 108.130 MPa). Specimens measuring 10 × 2 × 1 mm provided flexural strength values equivalent to those obtained in the sizes recommended by the ISO 4049 standard, with lower consumption of material, energy and time.

Shear bond strength of metal-ceramic repair systems.

This study evaluated the shear bond strength of different repair systems to nickel-chromium (NiCr) alloy after storage in water for either 24 hours or six months. One hundred cylindrical specimens (3 mm thick x 9 mm diameter) were fabricated using an NiCr alloy and embedded in a PVC ring, where they received one of five bonding and resin composite repair treatments (n = 20): Clearfil SE Bond/Clearfil AP-X (Group 1), Bistite II DC/Palfique (Group 2), CoJet/Z100 (Group 3), Scotchbond Multi-Purpose Plus/Z100 (Group 4; reference group), and CoJet Sand plus Scotchbond Multi-Purpose Plus/Z100 (Group 5). The specimens were stored in distilled water for 24 hours at 37 degrees C, thermocycled for 1,000 cycles in two baths (at 5 degrees C and 55 degrees C) with a dwell time of 30 seconds for each bath, and stored in distilled water at 37 degrees C for either 24 hours or six months. At 24 hours, Group 3 presented the highest mean values (P < 0.001); at six months, Group 5 demonstrated the highest mean values (P < 0.001). At six months, Group 5 presented a significant increase in shear bond strength (P < 0.001), while Groups 1 and 3 showed a significant reduction (P < 0.001). There were no significant differences between the storage times for Group 2 (P = 0.064) or Group 4 (P = 0.490).

Resistência à flexão de porcelanas feldspáticas convencionais processadas por injeção / Flexural strength of heat-pressing feldspathic porcelains

O objetivo deste estudo foi investigar o efeito do processamento por injeção (método da cera perdida) na resistência à flexão, em três pontos, de porcelanas feldspáticas convencionalmente obtidas por sinterização. Foram avaliadas as porcelanas Ceramco-2, Duceragold, Duceram-Plus, Excelsior, Omega-900, Symbio, Vitadur-Alpha e VMK-95. Como controle, foi também utilizada a porcelana Cergogold, fornecida na forma de pastilhas pré-sinterizadas e processada exclusivamente por injeção. Corpos de prova em forma de barra (n = 10), com dimensões de 25 × 5 × 2 mm (ISO-6872), foram confeccionados em matrizes metálicas e processados, por sinterização ou injeção, nas temperaturas de cocção indicadas pelos fabricantes. Os ensaios foram realizados em equipamento MTS-810 (Material Test System, EUA), com célula de carga de 10 kN e velocidade de 0,5 mm.min-1. Os resultados, submetidos à análise de variância (p menor ou igual a 0,05), mostraram que o processamento por injeção foi capaz de proporcionar maior resistência à fexão para as porcelanas Duceram-Plus, Excelsior, Omega-900, Symbio e VMK-95 (p < 0,001). Nessa mesma condição experimental, a porcelana Cergogold mostrou-se estatisticamente superior apenas à porcelana Vitadur-Alpha, sendo inferior à porcelana Omega-900 e semelhante às demais (p < 0,001). A resistência à fexão das porcelanas Ceramco-2, Duceragold e Vitadur-Alpha não foi influenciada pelo processo de obtenção (p < 0,001).

The aim of this study was to evaluate the effect of injection process, on the three-point flexural strength on feldspathic ceramic, fabricated by sintering technique. The ceramics evaluated were Duceragold, Duceram Plus, Excelsior, Omega 900, Symbio,Vitadur Alpha, VMK 95 and Ceramco 2. Cergogold, that the processing technique is based on a conventional injection moulding, was used for control. The bar-shaped specimens (n = 10) with the size of 25 × 5 × 2 mm (ISO-6872) were fabricated in a metal mould and processed by injection or sinterized, according to manufacturing specifcations. The fexural test was performed in a MTS 810 testing machine (Material Test System, USA), with a 10 kN load cell and a crosshead speed of 0.05 mm.min-1. The data (MPa) were subjected to analysis of variance (p less than or equal to 0.05), and showed that the injection processed enhance the flexural strength of Duceram-Plus, Excelsior, Omega-900, Symbio and VMK-95 (p < 0.001). In this experimental condition, the ceramic Cergogold showed high value than Vitadur-Alpha, was inferior to the ceramic Omega-900, but there were no signifcant difference with the others (p < 0.001). The flexural strength was not influenced by the processing method for the ceramics Ceramco-2, Duceragold and Vitadur-Alpha.

Avaliação mecânica das cerâmicas IPS-Empress 2 e In-Ceram Zircônia / Mechanical Evaluation of All-Ceramic IPS Empress 2 and In-Ceram Zirconia

O objetivo deste trabalho foi comparar a resistência à flexão em três pontos e a resistência à tração diametral do material de infra-estrutura dos sistemas cerâmicos IPS-Empress 2 (Ivoclar) e In-Ceram Zirconia (Vita). Para a realização do experimento, foram confeccionadas dez amostras de cada material para o ensaio de flexão (25mm x 5mm x 2mm)e 15 amostras para o ensaio de tração diametral (6mm x 3mm). Os testes foram realizados em equipamento MTS810 (Material Test System - EUA), com célula de carga de 10kN e velocidade de 0,5mm/minuto. Os resultados, após testes estatísticos de Mann-Whitney, mostraram que o In-Ceram Zirconia (434,17 MPa) apresentou maior resistência à flexão em relação ao IPS-Empress 2 (230,80 MPa). Entretanto, observou-se maior resistência à tração diametral doIPS-Empress 2 (175,41 MPa) em relação ao In-Ceram Zirconia (151,11 MPa). Pode-se concluir que a relação entre as duas propriedades não é a mesma para os materiais estudados e que a decisão pela indicação de um material não pode ser baseada em apenas uma propriedade mecânica.

Estudo in vitro da infiltração marginal em cavidades classe V restauradas com resinas compostas posteriores / In vitro study of marginal leakage in cavities class V restorations posterior composite

A proposta deste estudo foi verificar a infiltração marginal de cavidades classe V utilizando resinas compostas posteriores. Foram preparados na face vestibular de 30 incisivos bovinos, preparos cavitários classe padronizada com término em esmalte. Em seguida, os dentes foram divididos em três grupos e restaurados utilizando os materiais de acordo com as instruções dos fabricantes, ou seja: Grupo I: Etch&Prime 3.0 (Degussa) + Definite (Degussa); Grupo II: Admira Bond (Voco) + Prodigy Condensable (Kerr) e Grupo III: Admira Bond (Voco) + Admira (Voco). Após restaurados, os dentes foram submetidos a 500 ciclos térmicos e isolados com esmalte para unha. Após, foram imersos em solução de azul de metileno a 2% tamponado, por 2 horas. Em seguida, foram seccionadas e analisadas em lupa estereoscópica para qualificar os níveis de infiltração. Os resultados foram analisados estatisticamente pelo teste Kruskal Wallis. Observou-se escore médio de 1,45 para o Grupo III, apresentando estatisticamente menor infiltração marginal, seguido do Grupo II (2,70) e posteriormente Grupo I (3,45), os quais diferiram entre si. O sistema restaurador Admira Bond + Admira apresentou menor infiltração diante dos demais sistemas restauradores

Estudo do conteúdo de partícula inorgânica de resinas compostas diretas e indiretas / Study of the direct and indirect composite resin's inorganic contents

O propósito deste estudo foi avaliar o conteúdo de partícula inorgânica em massa e volume de resinas compostas de aplicação direta e indireta. Para a avaliação das partículas inorgânicas foram confeccionados cinco corpos-de-prova cilíndricos, com 5x2mm para cada material. Foram ativados por 40 segundos e pesados em balança analítica (Sartorius) à seco e imersos em água destilada. Após a eliminação da matriz orgânica realizada em forno elétrico a 700ºC por 3 horas, foram pesados à seco e armazenados em água destilada, por 7 dias para nova pesagem em imersão. O conteúdo por massa foi baseado na aplicação do Princípio de Arquimedes...

The influence of chemical activation on hardness of dual-curing resin cements.

During the cementation of metallic restorations, the polymerization of dual-curing resin cements depends exclusively on chemical activation. This study evaluated the influence of chemical activation compared with dual-curing (chemical and light activation), on the hardness of four dual-curing resin cements. In a darkened environment, equal weight proportions of base and catalyst pastes of the cements Scotchbond Resin Cement, Variolink II, Enforce and Panavia F were mixed and inserted into moulds with cavities of 4 mm in diameter and 2 mm in height. Subsequently, the cements were: 1) not exposed to light (chemical activation = self-cured groups) or 2) photoactivated (dual-curing = dual-cured groups). The Vickers hardness number was measured at 1 hour, 24 hours and 7 days after the start time of cements' spatulation. For all the cements, the hardness values of self-cured groups were lower than those of the respective dual-cured groups at 1 hour and 24 hours. At 7 days, this behavior continued for Variolink II and Panavia F, whilst for Scotchbond Resin Cement and Enforce there was no statistical difference between the two activation modes. All cements showed a significant increase in their hardness values from 1 hour to 7 days for both activation modes. Of the self-cured groups, Scotchbond Resin Cement and Variolink II presented the highest and the lowest hardness values, respectively, for all three times tested. Within the limitations of this study, up to the time of 24 h, chemical activation alone was unable to promote similar hardness as to that obtained with dual-curing.

Polimerização de resina composta com interposição de esmalte, dentina ou resina incisal / Polymeration of composite resin with interposition of enamel, dentin or incisal resin

Esse estudo avaliou, por meio de ensaios de dureza, a profundidade de polimerização de uma resina composta (TPH), após a interposição de camadas de esmalte, dentina ou resina incisal. As medidas de dureza foram efetuadas no primeiro e no segundo milímetro abaixo da superfície do compósito. De acordo com os resultados, os valores de dureza diminuíram com o aumento da profundidade e da espessura da camada interposta. Entretanto, para uma mesma espessura não houve diferença significativa para os valores de dureza, independentemente do material interposto

The influence of chemical activation on hardness of dual-curing resin cements

Na cimentação de restaurações metálicas, a polimerização dos cimentos resinosos duais depende exclusivamente da ativação química. Este estudo avaliou a influência da ativação química, comparada à dupla ativação (química e pela luz), na dureza de 4 cimentos resinosos duais. Em ambiente isento de luz, quantidades iguais em massa das pastas base e catalisadora dos cimentos Scotchbond Resin Cement, Variolink II, Enforce e Panavia F foram espatuladas e inseridas em matrizes com cavidade de 4 mm de diâmetro e 2 mm de altura. A seguir, os cimentos foram: 1) mantidos no escuro (ativação química = grupos quimicamente ativados) ou 2) fotopolimerizados (dupla ativação = grupos duais). A dureza Vickers foi obtida 1 hora, 24 horas e 7 dias após o início da espatulação dos cimentos. Em todos os cimentos, a dureza dos grupos quimicamente ativados foi menor que a dos respectivos grupos duais nos tempos de 1 hora e de 24 horas. Aos 7 dias, esse comportamento foi mantido pelo Variolink II e Panavia F, enquanto para o Scotchbond Resin Cement e para o Enforce não houve diferença estatisticamente significante entre os dois métodos de ativação. Todos os cimentos mostraram aumento significativo de dureza de 1 hora para 7 dias, em ambos os métodos de ativação. Dentre os grupos quimicamente ativados, o Scotchbond Resin Cement e o Variolink II mostraram, respectivamente, a maior e a menor dureza nos três tempos testados. Dentro dos limites deste estudo, até o período de 24 horas, a ativação exclusivamente química não foi capaz de promover dureza semelhante à obtida pela dupla ativação.

Cimentação de restaurações estéticas indiretas em posteriores / Cementation of indirect composit resins restaurations

Este estudo avaliou o grau de polimerização de um cimento resinoso dual (Variolink) após a interposição de duas diferentes resinas compostas indiretas (Artglass e Solidex). Corpos-de-prova em forma de disco (4 x 2mm) foram fotoativados por 40s através de uma camada de 2mm de espessura do material restaurador. A dureza foi mensurada imediatamente após a fotoativação após o armazenamento em ambiente a seco, ao abrigo de luz. De acordo com os resultados, os valores de dureza reduziram significativamente (p<0,05) superiores que os obtidos imediatamente após a fotoativação. Este estudo sugere que a ação do ativador químico de polimerização dos cimentos resinosos duais pode não ser suficiente e, conseqüentemente, seria necessário adotar uma criteriosa exposição à luz quando da utilização desses agentes de cimetação

Resistência à corrosão de ligas odontológicas submetidas à desinfecção / Corrosion resistance of dental alloys submitted to disinfection

O objetivo deste estudo foi avaliar o efeito da desinfecção ou esterilização sobre a resistência à corrosão de cinco tipos de ligas metálicas (Ag-Sn, Cu-Al, Cu-Zn, Ni-Cr e Co-Cr). Corpos-de-prova circulares (6 mm de diâmetro e 3 mm de altura, n = 150) foram fundidos,polidos e submetidos a um dos seguintes tratamentos: hipoclorito de sódio a 1% - 30 minutos; álcool 70 - 30 minutos; glutaraldeído a 2% - 30 minutos; glutaraldeído a 2% - 10 horas; estufa seca a 170 °C - 1 hora; autoclave - 120 °C - 20 minutos. Foram realizados seis ciclos de tratamento, simulando três etapas clínico/laboratoriais. Ao final, os espécimes foram armazenados em sulfeto de sódio a 0,25%, por 24 horas. A superfície foi analisada visualmente por dois examinadores e classificada segundo o seguinte critério: 0. ausência de alterações, 1. perda de brilho, 2. ligeira alteração de cor, 3. intensa alteração de cor, 4. corrosão generalizada. A análise revelou que asligas de cobre são mais susceptíveis à corrosão e as de Ni-Cr e Co-Cr as mais resistentes, ficando as de Ag-Sn em posição intermediária. O método menos agressivo foi o da estufa seca, seguida de glutaraldeído (30 minutos ou 10 horas) e álcool 70, enquanto o hipoclorito de sódio e a autoclavepromoveram maiores alterações.

Prevalência da proporção áurea na dentição natural / Prevalence the golden proportion in natural dentition

Considerando importância da estética na odontologia, incluindo a ênfase que vem sendo apontada pelos fabricantes, pela mídia e pelos profissionais da área, este trabalho foi idealizado com intuito de colaborar, fornecendo informações com relação à proporcionalidade entre os dentes anteriores superiores no sentido mésio-distal. Foram selecionados estudantes de odontologia, com dentição natural para verificação clínica da presença da proporção áurea entre os dentes, pelo método proposto po Levin. A amostra era composta por 120 indivíduos, sendo 62 do sexo masculino e 58 do sexo feminino. Do total, 75,8 por cento tinham seus dentes anteriores superiores em proporção áurea, sendo observado ainda que 96,55 por cento das mulheres apresentam proporção áurea, conta somente 56,45 por cento do homens. Ao final, concluiu-se que, a aplicação da proporção áurea é uma ferramenta interessante para reconstrução de dentes anteriores superiores, particularmente para pacientes do sexo feminino.